Abstract
Abstract In this study, butt welding of commercial AZ31 magnesium alloy sheets has been investigated by using the tungsten inert gas welding process with alternating and pulsed current. Magnesium alloy welding, although well developed and understood, can present some problems, such as porosity, hot cracking, oxide formation, etc. Samples of the welded parts have been examined by optic microscopy and mechanic tests. Results showed that porosities and homogeneous micro size oxides were rarely found. Orientation of the weld microstructure in direction of the heat transfer were also rarely observed and equiaxed grain morphology was the dominant grain structure as in the base metals. In addition, fusion zone and HAZ of the welded samples have generally shown twins. This seems to be a very dominant grain type particularly in pulsed samples. Hot cracking was not observed in any samples. Results of mechanical tests showed that pulsed current seems to generate more favorable higher mechanical properties of weld joints than alternating current for magnesium alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.