Abstract
Partial 1100, 1000, 900 and 700 °C isothermal sections of the Al–Rh–Ru phase diagram were determined. The isostructural binary AlRu and AlRh phases probably form a continuous β-range of the CsCl-type solid solutions. The Al 9Rh 2 and C-Al 5Rh 2 dissolve up to 4.5 and 13 at.% Ru, while Al 13Ru 4 and Al 2Ru dissolve up to 14.5 and 8 at.% Rh, respectively. A ternary orthorhombic structure ( Pbma, a = 2.34, b = 1.62 and c = 2.00 nm) related to the Al–Rh ɛ-phases was revealed at the extension of the Al–Rh ɛ-phase area at compositions up to Al 77Rh 15Ru 8.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.