Abstract
Due to its excellent comprehensive properties, glass fiber reinforced flame retardant PBT was widely applied in electrical accessory. In this paper, the recycled glass fiber reinforced flame retardant PBT（RGFFRPBT）with injection times effect on its carboxyl content, characteristic viscosity of PBT and the average length of glass fiber were studied. The properties of RGFFRPBT PBT including mechanical, thermal and rheological properties were well investigated. The results demonstrated that when GFFRPBT was injected third time, the length of glass fiber and characteristic viscosity of PBT decreased from 895um, 0.95 to 590um, 0.52, respectively. It also indicated that the decrease trend would accelerate with higher injection times. When the injection times were twice, the notched impact strength, flexural and tensile strength of RGFFRPBT-2nd decreased to 54J/m, 128MPa and 96.1MPa, respectively. Thermal stability, maximal crystallization temperature, melting point and HDT of RGFFRPBT-2nd were not significant differed to those of GFFRPBT. When the injection times were higher than three times, all of the properties decreased drastically. With the increasing of injection times, the samples show shear-thinning and nonlinear viscoelastic properties and the shear viscosity decreased, distinctly. The results illuminated that mechanical and thermal properties of RGFFRPBT-2nd were suitable to use in the electronic and electric field.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.