Abstract
This paper presents a detailed investigation on the fatigue response and damage progression in pseudo-ductile thin-ply angle-ply laminates with two configurations: an intermediate modulus-high modulus fibre combined IM-HM [±277/0]s and a standard modulus SM-SM [±266/0]s laminate. 80% of the “yield” stress was found to be the maximum stress for both laminates, where they can withstand 106 cycles without obvious damage or stiffness reduction. When laminates containing pre-fractured 0° plies were loaded in fatigue, both of the laminates showed a delamination dominated damage mode: the delamination initiated from the pre-fractured 0° plies and propagated at the interface between the 0° and angle plies with increasing number of cycles. An estimated delamination growth rate based on the stiffness reduction and delamination initiated from 0° ply fracture are also discussed. The IM-HM laminate with broken 0° fibres can still withstand fatigue loading at 80% severity without further modulus reduction or damage progression, whilst the SM-SM failed in delamination within a small number of cycles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Composites Part A: Applied Science and Manufacturing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.