Abstract
This work offers an analysis of the microstructure and the growth rate of an intermetallic compound within the aged AA 6061 aluminum alloy-304 stainless steel joint brazed with Zn-15Al and Zn-15Al-0.2Zr filler metals. The effect of zirconium addition on mechanical integrity of the brazed joint was studied. The experimental results confirm that the thickness of the Fe-Al intermetallic layer formed at the brazed seam/stainless steel interface increases with the increase of the aging time. Furthermore, it is established that the growth rate of the intermetallic layer for the Zn-15Al-0.2Zr brazed joint was lower than that for Zn-15Al. The results also indicate that the shear strength of both Zn-15Al and Zn-15Al-0.2Zr brazed joints decreases monotonously during aging. The value of the strength after aging lasting for 800 h for Zn-15Al and Zn-15Al-0.2Zr has decreased by 20 and 17%, respectively. The fracture of joints occurred at the interface between the brazed seam and the Fe4Al13 intermetallic layer. The morphology of the surfaces exhibits a cleavage fracture.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.