Abstract
A step-wise current-limiting flash sintering process (SCFS process) was proposed to densify La0.8Sr0.2Ga0.8Mg0.2O3-δ (LSGM) electrolyte. Well-densified microstructures of LSGM samples were obtained at 690 °C under an electric field of 100 V cm−1. Compared with the current-limiting flash sintering process, the spike in power dissipation was avoided, the shrinkage rate of LSGM samples was moderate, and the microstructures of LSGM samples were uniform. The conductivity of LSGM samples sintered via SCFS process at 0.9 A for 30 min reached 0.072 S cm−1 at 850 °C, and this was approximately the same as the value of conventionally sintered LSGM samples at 1400 °C for 10 h. These results proved that SCFS process achieved easy controllability, and it is expected that SCFS process can be applied in industry.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.