An Analytical Evaluation of the Effect of Weld Material Thickness on Residual Stresses Produced by Structural Weld Overlays on Pressurized Water Reactor Primary Cooling Piping

Abstract

Full Structural Weld Overlay (FSWOL) has been used successfully to mitigate intergranular stress corrosion cracking in boiling water reactor (BWR) welded stainless steel piping for many years. The FSWOL technique adds structural reinforcement, can add crack resistant material, and can create compressive residual stresses at the inside surface of the welded joint which reduces the possibility of further stress corrosion cracking. Recently, the FSWOL has been applied as a preemptive measure to prevent primary water stress corrosion cracking (PWSCC) in pressurized water reactors (PWR) on susceptible welded pipes with dissimilar metal welds common to PWR primary cooling piping. This study uses finite element models to evaluate the likely residual and operating stress profiles remaining after FSWOL and describes the results of sensitivity studies which were performed to examine the effect of weld overlay thickness on the residual stresses for typical dissimilar metal weld configurations.