An Ab Initio Investigation of CdSnN2Under Uniaxial Compressions

Abstract

Herein, the behaviors of CdSnN2are computationally investigated under uniaxial compressions based on density functional theory (DFT) calculations and a DFT‐1/2 scheme. When the compression is in [100] direction, phase transition is observed fromPna21toPnmaphase when the compression is larger than 30 GPa, while no phase change is observed for uniaxial compressions along [010] and [001] directions. For the former one, the bandgap first increases with a maximum at 20 GPa, followed with a reduction upon the critical pressure and nearly a constant above 30 GPa. The bulk modulus nearly increases monotonically except for the transit region from 20 to 29 GPa, and the shear modulus decreases to 29 GPa and then increases forPnmaphase. When compression is along [010] direction, the bandgap nearly remains around 0.620 eV. The bulk modulus increases with a maximum around 25 GPa and then decreases, while the shear modulus monotonically decreases. The bandgap first increases and then shrinks monotonically with increasing compression in [001] direction. The bulk modulus monotonically increases and the shear modulus decreases. The absorption is then calculated and discussed. The anisotropic behaviors of CdSnN2may hence indicate some potential applications.