Abstract

Unique precipitates with novel structures have been found in melt-quenched (MQ) Mg 98 Cu 1 Gd 1 alloys by transmission electron microscopy (TEM). Amorphous spherical particles with 50-200 nm sizes are uniformly embedded in Mg grains of an MQ Mg 98 Cu 1 Gd 1 alloy prepared with a relatively higher cooling rate. So-called LAL precipitates, which consist of an amorphous core sandwiched by long period stacking (LPS) phase, are formed in an MQ Mg 98 Cu 1 Gd 1 alloy prepared with a lower cooling rate. TEM observations show that LAL precipitates transform into LPS phases by annealing above 450 K. DSC results show that amorphous cores in LAL particles and amorphous particles crystallize at around 450 K, and partial melting of the LPS phase occurs at around 710 K prior to the melting of the Mg matrix. The composition of amorphous particles is 68 at%Mg, 26 at%Cu and 6 at%Gd, which is close to that having the highest glass forming ability (Mg 65 Cu 25 Gd 10 ). Limited solubility of Cu and Gd in Mg and large negative mixing enthalpy between Cu and Gd are responsible for the formation of unique precipitates in rapidly solidified Mg-Cu-Gd alloys.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.