Abstract
It is reported that Nd-Fe-Co-Al amorphous alloys have high bulk amorphous formation ability and high coercivity by rapid solidification method. We have examined the undercooling solidification, bulk amorphous formation and high coercivity appearance by using containerless process. In this study, we investigated the undercooling, bulk amorphous formation and magnetic properties for Nd-Fe-Co-Al alloys which are levitated and solidified by using the gas jet flow and high cooling type electromagnetic levitation system. Therefore, the high undercooling degree was 66–152 K and the samples formed amorphous phase. The bulk samples, � 6 mm sphere, solidified at the cooling rate, about 100 K/s. In addition, the coercivity for Nd65Fe10Co15Al10 sample with bulk amorphous phase, 3.7 kOe, was the highest value in all samples. Also, the thermal stability for Nd65Fe10Co15Al10 sample was carried out by isothermal annealing experiments. The origin of high coercivity may be related to the amorphous phase. [doi:10.2320/matertrans.47.2842]
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.