Aluminum-induced crystallization of amorphous silicon films deposited by hot wire chemical vapor deposition on glass substrates

Abstract

Aluminum-induced crystallization of amorphous silicon films is discussed. Amorphous Si films were deposited by hot wire chemical vapor deposition onto Al coated glass substrates at 430 °C. Complete crystallization of a-Si films was achieved during a-Si deposition by controlling Al and Si layer thicknesses. The grain structure of the poly-Si films formed on glass substrate was evaluated by optical and electron microscopy. Continuous poly-Si films were obtained using Al layers with a thickness of 500 nm or less. The average grain size was found to be 10–15 μm, corresponding to a grain size/thickness ratio greater than 20.