Abstract
Objectives. Determine the necessary conditions for obtaining a granulated η-Al2O3 carrier, investigate its structural and strength properties, and evaluate its activity for the model n-butane isomerization reaction.Methods. Samples containing bayerite structure aluminum trihydroxide were synthesized by precipitation from aqueous solutions of aluminum nitrate with ammonia under isothermal conditions at a constant pH value. The samples of the granulated carrier were obtained using an extrusion method when the composition of molding pastes was varied by tuning the ratio of bayerite- and η-Al2O3 -containing components and introducing polyvinyl alcohol.Results. The influence of the preparation conditions on the structural and strength properties of the active Al2O3 granules is evaluated. Samples of the aluminum oxide carrier were tested for a model reaction of low-temperature isomerization of n-butane, demonstrating a sufficiently high selectivity and reasonable prospects for use as catalysts for low-temperature isomerization of hydrocarbons.Conclusions. Increasing the content of the polyvinyl alcohol in the molding paste from 0.4 to 1.8 wt % is accompanied by an increase in the predominant sizes of the mesopores in the range of 10–50 nm and pores in the range of 50–80 nm, explaining the high values of all recorded parameters for the process of isomerization of n-butane.
Highlights
The samples of the granulated carrier were obtained using an extrusion method when the composition of molding pastes was varied by tuning the ratio of bayerite- and η-Al2O3-containing components and introducing polyvinyl alcohol
Summary data table of the porous structure of synthesized carriers studied by nitrogen porosimetry at 77 K using an Autosorb 6iSA unit
На основании проведенных испытаний носителей в модельном процессе изомеризации н-бутана выявлено, что полученные образцы алюмооксидного носителя, отличающиеся соотношением исходных байерит- и Al2О3-содержащих компонентов, имеют приблизительно одинаковую и достаточно высокую селективность и перспективны в качестве носителей катализаторов низкотемпературной изомеризации углеводородов
Summary
Determine the necessary conditions for obtaining a granulated η-Al2O3 carrier, investigate its structural and strength properties, and evaluate its activity for the model n-butane isomerization reaction. The samples of the granulated carrier were obtained using an extrusion method when the composition of molding pastes was varied by tuning the ratio of bayerite- and η-Al2O3-containing components and introducing polyvinyl alcohol. В качестве носителей для алюмоплатиновых катализаторов широко используется оксид алюминия, в частности его модификации: γ- и η-Al2O3. Обнаружено, что это свойство проявляется в значительно большей мере у формовочных паст из байерита, осаждаемого из солей алюминия аммиаком, по сравнению с таковым, полученным с использованием гидроксида натрия в качестве осадителя. Поэтому приоритетным является осаждение байерита аммиаком, при этом высокая структурированность паст, получаемых из гидроксида, осложняет процесс их экструдирования и ставит задачу нахождения условий приготовления гранулированного оксида η-Al2O3, соответствующего требованиям пригодности для катализатора изомеризации углеводородов, в том числе по примеси натрия. Цель настоящей работы состояла в определении условий получения гранулированного η-Al2O3-носителя, исследовании его структурно-прочностных свойств и оценке активности в модельном процессе изомеризации н-бутана
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call