Abstract
The performances of carbonated steel slag products in hydrochloric acid (HCl) solutions with pH = 1-5 for 56 days were studied and compared to conventionally cured ordinary Portland cement (OPC) specimens. The compressive strength of specimens and pH of solutions were monitored at different ages. The final microstructural modifications at pH = 1 were characterized by micro tests including X-ray diffraction (XRD), the Rietveld method (QXRD), fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA) and scanning electron microscopy (SEM). The ease of minerals to react with HCl was analyzed by thermodynamics. The micro test results revealed that carbonated steel slag products suffered more serious degradation than OPC. The alteration mechanisms of both included almost complete decalcification, dissolution of some crystallized or amorphous phases and the formation of silica gel. The thermodynamic analysis showed that ettringite had the highest potential to react with HCl while the CaCO3 had the lowest ability among the mineral phases studied.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.