Abstract
Al18B4O33 whisker reinforced Al, Mg alloy composites were prepared by a squeeze casting process. The interaction among the interface structure, heat stability and strength of the composites was analyzed. In the pure Al matrix composite, the interfacial reaction occurred only at a temperature higher than 750°C and its reaction products are γ-Al2O3. Interfaces between the whisker and reaction products have a preferred orientation with little mismatch. In the AC8A matrix composite, MgAl2O4 with a spinel structure was produced at the interface at a temperature higher than 500°C. These reaction products were shaped rectangularly. These reactions lead to the corrosion and shortening of the whiskers. It causes the degradation of the bending strength of the composites. In the AZ91D matrix composites, the reaction products are MgAl2O4 layers with a uniform thickness. This layer prevents the direct reaction between the whisker and the matrix. Consequently the whiskers are scarcely damaged and the composites have a good bending strength at high temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.