Abstract

Fabrication of all-solid-state Li battery has been strongly required to overcome safety issue of present Li battery. One of promising structures for ceramics electrolyte in all-solid-state battery is 2-layered structure composed of 3 dimensionally ordered macroporous layer (3DOM) and dense layer. In this study, we prepared Li0.35La0.55TiO3 (LLT) ceramics electrolyte with the 2-layered structure by suspension filtration method. Thicknesses of the dense and the porous layers were about 23 and 105 μm, respectively. The porous layer involved uniform pores of 1.8 μm in diameter. An electrochemical property of LiMn2O4 / 2-layered LLT composite, prepared by impregnation of precursor sol for LiMn2O4 into the pores followed by calcination, was tested. A rechargeable behavior of the composite electrode was clearly observed. From this result, it can be said that the composite can work as rechargeable battery. The discharge capacity of the composite was 27 mA h g-1.© (2011) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.