Abstract
Electrical insulation of the structural material is necessary to reduce the MHD pressure drop in a self-cooled liquid metal blanket. This coating has to be compatible with liquid Pb 17Li up to 450°C. Specimens with different types of coatings were exposed to static Pb 17Li for 1200 h at 450°C in order to study their compatibility. Iron and a ferritic steel were coated with an aluminide layer by means of an aluminizing process. Iron metal plate was hot dip aluminized at Thyssen, Germany. The preheated sheet was coated for this purpose by exposing for a few seconds to a melt of Al with 10 wt% Si. The ferritic steel, MANET, was immersed into a melt of the same composition. In this case, cold specimens were dipped into the melt at 700°C for up to 10 min. The formation of the required oxide scale on top of the aluminide layer was performed by using two different methods: high temperature oxidation in air and anodic oxidation at room temperature. All the exposed specimens were examined before and after the corrosion experiments. The analytical method used is EDX measurements on the cut of the specimens and metallographical examinations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.