Abstract
The microstructures and mechanical properties of three different cast Mo-5X (X = Zr, Ti, V) alloys were investigated. The alloys Mo-5Ti and Mo-5V show a single-phase solid solution microstructure, whereas the Mo-5Zr alloy exhibits polycrystalline Mo2Zr phases embedded in the Mo(Zr) solid solution matrix. Microhardness measurements were carried out by the Vickers indentation method. Compared to the single-phase solid solution alloys the Mo2Zr precipitations in Mo-5Zr result in the highest microhardness. Based on a well-known solid solution model it was shown that Zr, Ti and V are effective solid solution strengtheners. Additionally, constant displacement tests in the compressive mode between room temperature and 1100 °C confirm these findings. However, the homogeneously distributed Mo2Zr phases offer an extraordinary potential to improve the high temperature strength of Mo-based alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.