Abstract
The intentional tailoring of surface structure in bimetallic nanoparticles is of high interest for academic research and industry, and many attempts have been made to improve the control over the distribution mode of the constituent elements which ranges from homogeneously mixed nanoalloys to core–shell nanostructures. However, some metal combinations exhibit a wide miscibility gap in the bulk, which nonetheless could be overcome under definite conditions at the nanoscale due to size effects. Here we present the detailed XPS/STM investigation of alloying capability of bulk-immiscible metals on the example of the Ag-Pt/HOPG bimetallic system prepared by thermal vacuum deposition. We found out that partial alloying of Ag and Pt occurs already at the preparation stage, and the following thermal annealing of the Ag-Pt/HOPG samples at 300–400 °C does not help to enhance the alloying degree owing to thermodynamically driven surface segregation of silver. Increasing the annealing temperature ruins the structure of Ag-Pt bimetallic nanoparticles due to silver sublimation, while even longer annealing time leads to partial phase separation. Our results demonstrate a limited alloying capability of Pt and Ag at the nanoscale which will be relevant for further research on the design and functioning of bimetallic catalysts containing bulk-immiscible metals.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.