Alliages de zirconium pour utilization dans la vapeur entre 400° et 500°C

Abstract

Basing our choice on previously published results as well as tests performed in this laboratory, a few alloying elements were selected for testing in ternary alloy combinations with zirconium. The object of this research was to evaluate their corrosion resistance in steam at elevated temperatures.The alloys, prepared as buttons of approximately 70 grams, were tested in the rolled and annealed condition in steam at 400°, 450° and 500°C. Particularly promising results were obtained with the ternary alloys Zr-Fe-V and Zr-Cu-V. The corrosion behaviour in steam at temperatures up to 550°C of these two alloy combinations was, therefore, systematically studied. These tests permitted the determination of the optimum compositions as well as the temperature limits of their use.A more detailed study of these alloys will be performed using small ingots (10–20 kg). Résumé En partant des résultats publiés et d'essais effectués en laboratoire, un petit nombre d'éléments d'addition ont été selectionnés, puis expérimentés en combinaison ternaire avec le zirconium, en vue d'éprouver leur résistance à la corrosion par la vapeur à haute température.Les alliages pré parés sous forme de boutons de 70 g environ ont été transformés puis testés à l'état de plaquettes laminées et recuites dans la vapeur à 400°, 450° et 500°C. Des résultats particuliérement favorables ont été obtenus avec les ternaires Zr-Fe-V et Zr-Cu-V. Ces deux types d'alliage ont donc été retenus pour des essais systématiques en vapeur jusqu'à 550°C. Ces essais ont permis de déterminer les compositions optimales et les limites de température d'utilisation.Par la suite, les alliages ainsi définis seront étudiés de façon plus approfondie à partir de petits lingots de l0 à 20 kg.