Aligned CNx nanotubes by pyrolysis of ferrocene/C60 under NH3 atmosphere

Abstract

Aligned CNx (x<0.1) nanotubes have been generated by pyrolyzing ferrocene/C60 mixtures at 1050 °C in an ammonia atmosphere. The structure and composition of the product were determined by high-resolution transmission electron microscopy and high spatial resolution electron energy-loss spectroscopy. The CNx tubes (15–70 nm diameter, <50 μm length) grown in large flakes (<3 mm2) consist of a reduced number of “graphitic” layers (<15 on either side) arranged in a bamboo-like structure. Areas of high nitrogen concentration were found within curved or corrugated “graphite-like” domains. The observation of a well-developed double peak in the σ* feature of the N K-edge suggests that the material has not undergone the transition to the fullerene-like phase known for nitrogenated carbons. Incorporation of nitrogen from the gas phase (NH3) into CNx nanotubes therefore leads to improved and more efficient N substitution into the network as compared to the synthesis with solid nitrogen-containing precursors reported earlier.