AlGaN/GaN Metal–Oxide–Semiconductor High-Electron Mobility Transistors Using Oxide Insulator Grown by Photoelectrochemical Oxidation Method

Abstract

A photoelectrochemical oxidation method was used to directly grow oxide layer on AlGaN surface. The annealed oxide layer exhibited beta-Ga <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> and alpha-Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> crystalline phases. Using a photoassisted capacitance-voltage method, a low average interface-state density of 5.1 times 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">11</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> . eV <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> was estimated. The directly grown oxide layer was used as gate insulator for AlGaN/GaN MOS high-electron mobility transistors (MOS-HEMTs). The threshold voltage of MOS-HEMT devices is -5 V. The gate leakage currents are 50 and 2 pA at forward gate bias of VGS = 10 V and reverse gate bias of V <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">GS</sub> = -10 V, respectively. The maximum value of g <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">m</sub> is 50 mS/mm of VGs biased at -2.09 V.