Abstract
AlCoCrFeNiTi-C High Entropy Alloy (HEA) develops a single BCC phase after 10 h of milling. Sintering at 1000 °C promotes the formation of NiAl rich B2, CrFe disordered BCC and TiC phases making the alloy a dual phase structure with TiC precipitates. Alloy also exhibits a good room temperature compressive strength of 2503 ± 8 MPa and hardness of 910 ± HV0.5 which can be attributed to the presence of nano sized TiC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.