Abstract
The Al 2O 3/SiC nanocomposites containing 3–8 vol.% SiC were prepared through infiltration and in situ thermal decomposition of a preceramic polymer SiC precursor (poly(allyl)carbosilane) in pre-sintered alumina matrix. The volume fraction of SiC, and the microstructure of composites were adjusted by concentration of the polymer solution, and by the conditions of pyrolysis and sintering. The specimens were densified by pressureless sintering at temperatures between 1550 and 1850 °C in flowing argon. The use of powder bed producing SiO, CO and other volatile species suppressed decomposition reactions in the composites and was vital for their successful densification. The experimental results are discussed against thermodynamic analysis of the system Al 2O 3/SiC/SiO 2 in an inert Ar atmosphere.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.