Abstract
The penetration, softening point, and ductility of the aging basic asphalt and styrene-butadiene-styrene (SBS) modified asphalt were studied, and the thin film oven aging behavior of them was researched by using infrared spectrum. The experimental results showed that the softening point was increased, the penetration and ductility were decreased after basic asphalt thin film oven aging; the results of aging SBS modified asphalt thin film oven aging was similar too. The research of infrared spectrum indicated that absorbing–oxygen oxidation reaction was taking place when basic asphalt film was aging, carbonyl and sulfoxide groups were increased after SBS modified asphalt thin film oven had been aging. The aging extent of SBS modified asphalt was bigger than basic asphalt and the ability of bearing low temperature was better. SBS modified asphalt could have worse anti-aging performances than that of base asphalt.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call