Abstract
AbstractThe aging of an uncured, DGEBA‐based commercial film adhesive exposed to high humidity at 40°C was monitored by high performance liquid chromatography (HPLC), thermal analysis, solubility, flow, and mechanical testing of joints. DGEBA and brominated DGEBA resins, and representative mixes of these were hydrolyzed in vitro. It is suggested that the major reaction at 40°C is polymerization, which is accelerated by moisture and leads to a crosslinked structure different to that resulting from normal cure. The poorer adhesive performance after aging is mainly the result of reduced resin flow during joint formation, although there is some contribution from the hydrolysis of epoxide groups which leads to lower crosslink density in the cured adhesive. The softening point of the uncured material and Tg of the cured material are useful indicators of the quality of this adhesive which, compared to some earlier formulations, has improved resistance to these conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.