Abstract
The poly(propylene imine) dendrimer DAB-dendr- (NH2)8 was hydrophobically modified with dodecanoyl end groups. The modified dendrimer was deposited onto mica by adsorption from solution and observed by atomic force microscopy. With the decrease of adsorption time, the modified dendrimer varied from continuous film to scattered islands. For the adsorption time of 20s the dendrimer formed a sub-monolayer thin film that contained many fractal aggregates of fractal dimension 1.80 that were > 1 microm in diameter and no more than 0.8nm thick. After 5 months at 1#1 , the initial fractal aggregates transformed into disks and other less-branched shapes with average heights of the domains of 0.6nm and 0.4nm, respectively. Formation of the fractal aggregates is explained by diffusion-limited aggregation. The slow reorganization of dendrimer molecules in the fractal aggregates occurs at a temperature well above the Tg of the dendrimer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.