Abstract
AbstractThe ageing behavior due to the effects of heat, ozone, γ‐ radiation, and water on ethylene propylene diene monomer rubber/styrene butadiene rubber (EPDM/SBR) blends was studied. The tensile strength, crack initiation, ozone ageing, gamma radiation, and water resistance of the blends were measured and used to determine the extent of ageing. Tensile strength of blends of different compositions increased after thermal ageing for 96 h at 100°C probably due to the continued cross‐linking. It has been observed that an increase in EPDM in the blends improves the ozone resistance of the blends. Crack initiation was noted only in blends with lesser amount of EPDM and the cracks in such blends were found deeper, wider and continuous. With 15 kGy irradiation dose, the tensile strength of the blends found to be decreased while it increased with 80 kGy dosage of γ‐radiation. The elongation at break showed a decreasing trend with increased dosage of γ‐radiation. It has also been observed that the EPDM rich blends showed negligible water uptake. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.