Abstract
Microstructure and ageing characteristics of a cast Zn-Al based alloy (ZnAl7Cu3) were studied using X-ray diffraction, electron scanning microscopy and back-scattered diffraction techniques. Two stages of phase transformation, i.e., decomposition of zinc rich η phase and four phase transformation, α + e → T′ + η, were detected during ageing at 150°C. Electron back-scattered diffraction technique was applied in distinguishing both zinc rich η and e phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.