Abstract

Advanced transmission electron microscopy techniques were carried out in order to investigate stress corrosion cracking in Alloy 600 U-bend samples exposed in simulated PWR primary water at 330 °C. Using high-resolution imaging and fine-probe chemical analysis methods, ultrafine size oxides present inside cracks and intergranular attacks were nanoscale characterized. Results revealed predominance of Cr 2O 3 oxide and Ni-rich metal zones at the majority of encountered crack tip areas and at leading edge of intergranular attacks. However, NiO-structure oxide was predominant far from crack tip zones and within cracks propagating along twin boundaries and inside grains. These observations permit to suggest a mechanism for intergranular stress corrosion cracking of Alloy 600 in PWR primary water. Indeed, the results suggest that stress corrosion cracking is depending on chromium oxide growth in the grain boundary. Oxide growth seems to be dependent on oxygen diffusion in porous oxide and chromium diffusion in strained alloy and in grain boundary beyond crack tip. Strain could promote transport kinetic and oxide formation by increasing defaults rate like dislocations.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.