Adsorption of cadmium (II) on organic xerogel microspheres: effect of adding sepiolite or vermiculite and operating conditions on the adsorption capacity.

Abstract

The organic xerogel (OX) was synthesized through sol-gel polymerization of formaldehyde and resorcinol in inverse emulsion using Na2CO3 as a catalyst. Meanwhile, OX containing sepiolite (OX-Sep) and vermiculite (OX-Ver) were prepared similarly to OX but adding clays during synthesis. All materials were mesoporous and presented spherical morphology, and the surface of these materials exhibited an acidic character because the concentration of acidic sites was higher than those of basic sites. Cd(II) adsorption from aqueous solutions onto OX, OX-Sep, and OX-Ver was examined, and the OX-Sep showed the highest adsorption capacity towards Cd(II) of 189.7mg/g, being 1.5, 2, and 36 times higher than that of OX-Ver, OX, and Sep. The OX-Sep capacity for adsorbing Cd(II) was significantly lessened by decreasing the pH from 7 to 4 and raising the ionic strength from 0.01 N to 0.1 N. This trend was ascribed to electrostatic attraction between the Cd+2 in water and the negatively charged surface of OX-Sep. Besides, desorption studies at pH 4 showed that the average desorption percentage of Cd(II) adsorbed on OX-Sep was 80%. The characterization results and the effect of the operating conditions on the adsorption capacity proved that electrostatic attraction and cation exchange play a crucial role in the adsorption mechanism.