Abstract
AbstractThe adjacent relation of primary phase fields and corresponding invariant reactions of the system CaO‐SiO2‐Nb2O5‐La2O3 are of great importance for the study on its phase diagram. In the present work, the phase equilibrium in the high w(La2O3) region of CaO‐SiO2‐Nb2O5‐La2O3 system was studied by thermodynamic equilibrium experiment. The adjacent relation of primary phase fields was determined and represented in the form of adjacent tetrahedrons. The Alkemade Rule applicable to quaternary phase diagram was deduced, which can be used to infer the liquidus temperature trend on univariant curves. The rule was then used to determine the possible temperature range of invariant reactions corresponding to the adjacent tetrahedron in CaO‐SiO2‐Nb2O5‐La2O3 system, and the result was shown in the form of Schairer diagram. Finally, the reaction types of five invariant points were determined according to the Lever Rule for quaternary phase diagram, including:① L1+CaO·3SiO2·2La2O3→CaO·SiO2+SiO2+La2O3·Nb2O5,② L2→CaO·SiO2+La2O3·Nb2O5+SiO2+CaO·Nb2O5,③ L3+CaO·3SiO2·2La2O3+2CaO·Nb2O5→10CaO·6SiO2·Nb2O5+La2O3·Nb2O5,④ L4+10CaO·6SiO2·Nb2O5→CaO·SiO2+2CaO·Nb2O5+La2O3·Nb2O5,⑤ L5+2CaO·Nb2O5→CaO·Nb2O5+La2O3·Nb2O5+CaO·SiO2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.