Abstract
[Ti0.2C0.8/a-C]40 multilayer thin films composed of forty pairs of TiC and pure carbon layers were formed on a selective laser melted (SLM) martensitic stainless steel by means of ion-plasma deposition process. SLM steel was pre-treated by one of the two following schemes: (1) oil quenching from 1040°C followed by heating to 480°C for 4 hours and air cooling (HT), finish milling (FM); (2) HT, FM, ion-plasma nitriding followed by burnishing. Mechanical failure mode and critical load Lc for damaging the coatings were determined using linear scratch tests performed at linearly-increased normal force. Indentation by conical diamond tip were carried out in order to asses an elastic recovery and energy dissipation coefficient defined as the ratio of plastic to total deformation energy. The scratch test results showed that the post-processing of the substrate strongly influenced the failure mode of the coating and increased the critical load from 320 mN to 920 mN. Indentation revealed that nitriding and burnishing before coating deposition increase the elastic recovery of the [Ti0.2C0.8/a-C]40 coating-substrate system from 24% to 68%. The energy dissipation coefficient drops from 79% to 45%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.