Abstract
Laser surface texturing and micro-arc oxidation provide excellent approaches to enhance the adhesion strength and anti-corrosion performance of adhesive bonding interfaces in aluminum alloys, which can be applied in the field of automotive light weighting. Herein, micro-arc oxidation coatings were fabricated on the laser-textured aluminum surface under the voltage of 500 V for various treatment times (5 min, 15 min, 30 min, 60 min). The anti-corrosion performance of ceramic coatings on the laser-textured surface was analyzed using electrochemical measurements. The results of electrochemical measurement indicate that the coating on the sample surface presents two time constants corresponding to a dual-layer structure. The sample grown under 500 V for 60 min exhibits excellent protective performance with a value of 1.3 × 107 ohm·cm2. The adhesion strength of laser-textured ceramic coating is improved compared with the as-received substrate. The sample treated with 500 V for 30 min exhibits the highest bonding strength with a value of 52 MPa. The wider pores and bulges for the sample grown in 60 min would introduce microcracks and consequently reduce the adhesion strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.