Abstract
The effect of firing conditions on the adherence of a glass-bonded Pt-Au printed thick film conductor to a 96 wt % Al2O3 substrate was determined by a fracture mechanics measurement of the critical fracture energy for catastrophic thick film-substrate separation. The technique also demonstrated that separation by slow crack growth (delayed failure) occurred in this system. Analysis of the thick film microstructure and fracture surfaces showed that optimum adherence was primarily a result of a mechanically interlocked interface formed between the conductor metal and the glass bonding layer which, in turn, was strongly bonded to the alumina substrate. The two step decrease observed inγIC (from 3.7 to 0.2 J m−2) with firing temperatures over 860° C resulted from the removal of this interlocking metal-glass interface brought on by metal sintering and glass migration to the substrate. Thus, at 860° C firing temperatures, adherence is controlled by cohesive fracture in the glass bonding phase while above 1000° C it is controlled by adhesive failure of the weak chemical-physical bond at the metal-glass interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.