Abstract
IntroductionCalcium silicate cements (CSCs) with the addition of nanohydroxyapatite and calcium carbonate play a critical role in dental applications. To further improve their properties, particularly radiopacity and biointeractivity, the fluoride-containing radiopacifier ytterbium trifluoride (YbF3) was added to their composition, and biological and mechanical characteristics were evaluated. MethodsYbF3 was added to 3 different CSCs: cement I (CSC + calcium carbonate), cement II (CSC + nanohydroxyapatite), and Portland cement. Material characterization encompassed measurements of pH, calcium, ytterbium, and fluoride ion release; radiopacity; setting time; porosity; microindentation properties; wettability; and Fourier transform infrared spectroscopic, x-ray diffraction, and scanning electron microscopic analyses. Osteoblast- and osteoclast-like cells were grown on the materials' surface to evaluate their adherence. ResultsThe addition of calcium carbonate, nanohydroxyapatite, and 30 wt% of YbF3 improved radiopacity and the setting time of experimental cements. The pH values did not differ among the groups. The greatest ytterbium and fluoride releases occurred in the Portland cement + YbF3 group. Combined x-ray diffraction and Fourier transform infrared spectroscopic analysis showed the presence of calcium hydroxide and calcium silicate hydrates. In addition, the presence of calcium ytterbium fluoride and ytterbium oxide proved that YbF3 reacted with cement compounds. Wettability of cement I + YbF3 was superior to other formulations, but its porosity and microindentation properties were weaker than in the Portland cement + YbF3 mixture. Cement II + YbF3 presented micromechanical indentation and porosity characteristics similar to the Portland-based cement formulation. Osteoclast- and osteoblast-like cells adhered to the cements' surfaces without alteration of the cell structural integrity. ConclusionsYbF3-containing CSCs with nanostructured hydroxyapatite and calcium carbonate are well suited for dental application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.