Abstract
The electrocatalytic activity of Pt3Ru2/C nanocatalyst toward the electro-oxidation of bulk CO was examined in acid and alkaline solution at ambient temperature using the thin-film, rotating disk electrode (RDE) method. The catalyst was characterized by XRD analysis. The XRD pattern revealed that the Pt3Ru2/C catalyst consisted of two structures, i.e., Pt-Ru-fcc and Ruhcp (a solid solution of Ru in Pt and a small amount of Ru or a solid solution of Pt in Ru). Electrocatalytic activities were measured by applying potentiodynamic and steady state techniques. The oxidation of CO on the Pt3Ru2/C catalyst was influenced by pH and anions from the supporting electrolytes. The Pt3Ru2/C was more active in alkaline than in acid solution, as well as in perchloric than in sulfuric acid. Comparison of CO oxidation on Pt3Ru2/C and Pt/C revealed that the Pt3Ru2/C was more active than Pt/C in acid solution, while both catalysts had a similar activity in alkaline solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.