Abstract
A Ni-rich Pt-Ni alloy was synthesized via a solvothermal method and transformed into platinum-nickel nanocage catalysts (PNCs) by applying a two-phase corrosion process. The catalysts were physically and electrochemically characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) and both cyclic and linear sweep voltammetry using a rotating disk electrode (RDE). During the RDE testing, the half-wave potential of the PNC was 30mV higher compared to that of a commercial Pt/C catalyst for the oxygen reduction reaction (ORR). The RDE experiments showed that the specific and mass activity of the PNC was 2 and 4 times greater than Pt/C, respectively, at 0.9V. Catalyst-coated membranes (CCMs) were fabricated with the Pt-Ni nanocages using an automated air-assisted cylindrical liquid jet sprayer system. The PNC CCMs were loaded into proton exchange membrane fuel cells (PEMFC) for activity and stability testing. The CCMs showed no obvious Pt and Ni dissolution and redeposition in the membrane even after 30K cycles. The performance and electrochemically active surface area (ECSA) retention of the PNC was far superior to commercial Pt/C, just short of the US Department of Energy (DOE) 2020 targets, suggesting that Pt-alloy nanocages are very promising candidates for high-performing commercial PEMFCs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.