Abstract
Low-temperature deposited titanium nitride layers exhibiting increased and distorted lattices are subjected to in situ X-ray diffraction investigations at different temperatures. Annealing at about 450 °C leads to a complete lattice relaxation due to diffusion of point defects in the lattice. The activation energy for this diffusion can be calculated to be 1.23 ± 0.07 eV (while the reported activation energy of vacancy diffusion in TiN films is 2.09 eV). This proves that lattice widening and distortion in titanium nitride films deposited by dc magnetron sputtering at temperatures below 200 °C is mainly due to atoms on interstitial sites, and that the density of vacancies is high enough that most of the interstitial atoms find a vacancy to recombine, which leads to the observed relaxation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.