Abstract
Inorganic coatings are being developed to protect marble monuments and sculpture from weathering. In this work, the acid resistance of hydroxyapatite (HAP), calcium oxalate, and calcium tartrate coatings on Carrara marble were compared. To quantify the rate of attack on calcite, the pH of the solution was measured. This approach was validated by confirming that the rate of dissolution of untreated calcite inferred from the change in pH agrees with data in the literature. Calcium tartrate coatings were incomplete, and the mineral is so soluble that it offered no significant protection. Calcium oxalate forms coherent coatings, so it serves as a sacrificial coating in spite of having solubility comparable to that of calcite. HAP was deposited from aqueous solutions of 1M diammonium hydrogen phosphate (DAP), with or without millimolar additions of CaCl2 (which improved coverage) and (NH4)2CO3 (which resulted in cracking). The best HAP coatings remained porous; nevertheless, they were comparable to oxalate coatings in the short term and superior in the long term, reducing the dissolution rate by about 40%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.