Abstract
The finishing accuracy and efficiency of magnetic abrasive finishing (MAF) are mainly depending on magnetic abrasive powders (MAPs). A new kind of core–shell structured carbonyl iron powders (CI-MAPs) with a hard Fe/Al intermetallic shell for magnetic abrasive finishing is successfully synthesized by in-situ alloy-hardening the surface of spherical carbonyl iron powders in this study. The feasibility of such an in-situ alloy-hardening strategy is theoretically designed according to the Fe/Al intermetallic compound formation chemical reaction using the Gibbs free energy principle and the TG-DSC testing, and thus the experimental thermodynamics temperature and time ranges of such chemical reactions are proposed. Experimental results shown that a densely zigzag-like uniform alloy-hardening layer with a thickness of about 11 μm, which are composed of Fe3Al, FeAl, and Fe2Al5 intermetallic compounds, was in-situ chemically synthesized on the surface of the spherical carbonyl Fe powders. The achieved core–shell structured powder is performed to finishing a Zirconium tube experimentally, and the roughness (Ra) of the Zirconium tube is greatly improved from 0.361 μm to 0.085 μm by 3 MAF passes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.