Abstract
In this study, the high strength-ductility properties of wire-arc additive manufactured (WAAM) Al-Mg-Sc aluminum alloy were achieved by friction stir processing post-treatment (FSPPT) and high temperature aging treatment (HTAT). The FSPPT significantly refined the microstructure and eliminated porosity defects, which the average grain size was about 2.4 ± 0.2 μm in stirring zone (SZ). There was no obvious growth in grain size after HTAT and the average grain size was about 2.7 ± 0.4 μm in SZ. Many fine secondary Al3(Sc,Zr) phases were precipitated. Compared to WAAM sample, the average ultimate tensile strength (UTS), yield strength (YS) and elongation (EL) of FSPPT + HTAT sample increased by 57.9%, 54.7% and 205.9%, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.