Abstract
In this study, Mg-13.2Gd-4.3Ni alloys containing continuous bulk-shaped long-period stacking ordered (LPSO), lamellar LPSO, and a small amount of eutectic phase were prepared, and the evolution of microstructure at different extrusion temperatures and its influence on mechanical and degradation properties as well as corrosion mechanism were investigated. Preheating before extrusion can effectively promote the precipitation of lamellar LPSO in matrix. EX400 with higher volume fraction of non-DRXed grains exhibited higher strength, which was mainly due to strong texture, high dislocation density, and high volume fraction of lamellar LPSO. The EX420 with higher volume fraction of DRXed grains showed higher degradation rate, which was mainly due to the higher density of grain boundary. The EX400 exhibited excellent comprehensive properties with tensile yield strength (TYS) of 334 MPa, ultimate tensile strength (UTS) of 484 MPa and elongation (EL) of 7.4%, ultimate compressive strength (UCS) of 638 MPa and compressive yield strength (CYS) of 443 MPa, degradation rate of 86.1 mg/cm2/h at 93 °C in 3 wt.% KCl solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.