Abstract
To achieve a balanced combination of high strength and high plasticity in high-strength low-alloy (HSLA) steel through a hot-rolling process, post-heat treatment is essential. The effects of post-roll air cooling and oil quenching and subsequent tempering treatment on the microstructure and mechanical properties of HSLA steels were investigated, and the relevant strengthening and toughening mechanisms were analyzed. The microstructure after hot rolling consists of fine martensite and/or bainite with a high density of internal dislocations and lattice defects. Grain boundary strengthening and dislocation strengthening are the main strengthening mechanisms. After tempering, the specimens’ microstructures are dominated by tempered martensite, with fine carbides precipitated inside. The oil-quenched and tempered specimens exhibit tempering performance, with a yield strength (YS) of 1410.5 MPa, an ultimate tensile strength (UTS) of 1758.6 MPa, and an elongation of 15.02%, which realizes the optimization of the comprehensive performance of HSLA steel.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.