Abstract
Residual strain accumulation during thermal cycling of the Ti50Ni50 alloy under a constant stress of 200 MPa through the temperature range of complete and incomplete forward martensitic transformation was studied. The temperature range of the forward martensitic transformation during thermal cycling was chosen as 25, 50, 75, or 100% of the M s-M f interval measured in the first cycle. It was shown that intensive accumulation of residual strain took place in the last stage of the forward transformation. It was observed that resistivity increased more rapidly with an increase of the fraction of the temperature range of forward martensitic transformation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.