Abstract
A liquid hyperbranched polycarbosilane (LHBPCS) with stoichiometric C/Si ratio but without unsaturated groups was synthesized. Different from traditional thermal crosslinking, ultraviolet (UV) irradiation crosslinking was taken. The molecular weight, the consumption of SiH group and ceramic yield of LHBPCS showed an increase trend with increasing the UV irradiation time. After 30min of UV irradiation, 71.8wt% ceramic yield was obtained. In addition, extra divinyldimethylsilane was added into LHBPCS. Under UV irradiation, both the SiH group and vinyl group of divinyldimethylsilane were consumed. But the reaction extend of vinyl group was much faster than that of SiH group. Compared with pure LHBPCS, the mixture of LHBPCS and 5wt% divinyldimethylsilane gave a higher ceramic yield of 79wt% after 30min of UV irradiation. By heating the crosslinked LHBPCS to 1000°C, a near stoichiometric SiC ceramic was got. It exhibited excellent thermal stability at 1400°C in air.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.