Abstract
Carburizable martensitic stainless steels (MSSs) are attractive candidates for bearings due to their high corrosion resistance, high hardness, and high temperature performance. Wear performance in tribocorrosion applications is strongly influenced by the surrounding environment. Electrochemical testing was used to evaluate three different surface treatments on AMS 5930 steel developed for advanced gas turbine engine bearing applications: low temperature (LTT), high temperature (HTT), and carbonitrided (CN). HTT had a higher corrosion rate that increased with time, whereas LTT and CN had lower corrosion rates that were stable over time. Accelerated testing revealed that surface treatment significantly influenced how corrosion propagated: HTT was more uniform; conversely, LTT and CN showed localized attack. Degradation mechanisms developed from electrochemical methods provide rapid insight into long-term wear behavior.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.