Low temperature (T) ac magnetic susceptibility (χac) measurements were performed in powder samples of the Zn1−xFexO (x=0–0.078) prepared by a combustion reaction method. The amplitude of the ac magnetic field was kept constant (1mT) while its frequency (f) varied in the range 10–104Hz for 5≤T≤300K. The diluted samples presented cusps with maxima distributed around Tf=17.5±0.5K while no such feature was observed for the pure sample (x=0). The cusp was found to become more pronounced with the increasing Fe content. Also it decreased and shifted to higher values of T by increasing f. The shift in Tf was found to follow a Vogel–Fulcher law with Ea/kB=317.6K, T0=4.65K and τ0=10−14s, for the activation energy, critical temperature and characteristic time-constant, respectively. The energy gap of the sample was measured and they were found to vary in the range 3.75–3.80eV. The overall χac-data resembles those obtained for cluster spin-glass state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.