Abstract
The effect of YBCO adding on the superconducting of BPSCCO system with nominal starting composition of (Bi1.6Pb0.4Sr2Ca2Cu3O δ )1−x(YBCO) x with x = 0.00−0.10 was studied. The preparation methods used to prepare the samples are the conventional solid-state techniques. From the XRD data, it is observed that the percentage of the Bi-2223 phase increases and Bi-2212 decreases for addition x = 0.02–0.04, respectively. The effect of YBCO addition on the BPSCCO system also has been investigated in term of AC susceptibility study. We have studied the various applied field dependence of the AC susceptibility in polycrystalline samples. The AC susceptibility measurements in the range 0.05 to 2.00 Oe show that as the applied fields increases, the intergranular AC loss peaks move to lower temperature, and also height decreases and width increases. The effect of YBCO addition for the intergranular critical current J cm, and the presence of weak links that coupled the superconducting grains were defined.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.