Abstract
In this paper, we prepared Bi2223/Ag tapes with interfilamentary oxide barriers for filament decoupling and also for reducing AC losses under AC external magnetic field. To suppress the side effect on Bi2223 phase formation inside the filaments and superconducting properties in final tapes by introducing oxide barriers, we selected Ca <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> CuO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> as barrier materials. In addition, the 30 wt% Bi2212 powders were mixed into Ca <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> CuO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> , to improve their deformation properties for cold working such as drawing and flat rolling. The mixtures of Ca <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> CuO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> and Bi2212 were introduced around the twisted Bi2223 filaments. AC losses in barrier tapes under parallel transverse magnetic field were measured at 77 K, and compared with the several analytical models. Based on the results, the effect of barrier introduction on the AC loss characteristics in twisted multifilamentary tape is discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.