Abstract
The corrosion performance of Al-2024 substrates coated with an epoxy clear coating and a pigmented epoxy coating was investigated. The absorption of water in the pigmented coating was high compared to the clear coating. The clear coating provided a good barrier which is stable beyond 120 days of immersion in a 0.5 M NaCl solution. The shape of the Nyquist plot of the pigmented coating changed with immersion time and reveals the existence of physico-chemical processes in the coating and/or at the interface. Its impedance magnitude at low frequencies remained very high (~ 109 Ω.cm2) after 72 days of immersion in sodium chloride solution. Both coatings exhibited good dry adhesion on Al-2024. The wet adhesion of the clear coating was poor while the stress (~ 9 MPa) required in a pull off adhesion test of the wet pigmented coating remained high.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.